Evaluation of Local Stress for Stress Corrosion Crack Initiation by Three-Dimensional Polycrystal Model
Masayuki KAMAYA and Takayuki KITAMURA
Abstract:In order to understand the initiation behavior of microstructurally small cracks in a stress corrosion cracking condition, it is important to know the tensile normal stress acting on the grain boundary (normal G.B. stress). The local stress in a polycrystalline body is greatly influenced by deformation constraint which is caused by anisotropic and/or inhomogeneous property of each grain. In present study, the local normal G.B. stress on bi- and tri-crystal bodies and a three-dimensional polycrystalline body consisting of 100 grains were evaluated by the finite element method under a remote uniform tensile stress condition. The polycrystalline body was generated by using a Monte Carlo procedure and random orientations were assigned to each grain. It was revealed that the local normal G.B. stress on the polycrystalline body is inhomogeneous under uniform applied stress. The stress tends to be large near the triple points due to the deformation constraint caused by adjacent grains, even though the grain boundary inclination to the load axis has large influence. It was also shown that particular high stress was not observed at corners of the polycrystalline body. Key Words:Polycrystalline material, Crack initiation, Grain boundary, Stress corrosion cracking, Normal stress, Finite element analysis